Yakakwira Yakachena 99.95% YeAtomic Energy Indasitiri Yakanaka Plasticity Wear Resistance Tantalum Rod/Bar Tantalum Zvigadzirwa
Product Parameters
Product Name | 99.95% Tantalum ingot bar buyers ro5400 tantalum price |
Kuchena | 99.95% min |
Giredhi | R05200, R05400, R05252, RO5255, R05240 |
Standard | ASTM B365 |
Size | Dhiya(1~25)xMax3000mm |
Condition | 1.Kupisa-kwakakunguruka/Kutonhora-kukanyura;2.Alkaline Kuchenesa;3.Electrolytic Polish;4.Kugadzira, kukuya;5.Stress relief annealing. |
Mechanical property (Annealed) | Grade;Tensile simba min;Kubereka simba min;Elongation min,% |
(UNS), psi (MPa), psi(MPa)(2%), (1in. gage kureba) | |
(RO5200, RO5400), 30000 (207), 20000 (138), 20 | |
Ta-10W (RO5255), 70000 (482), 60000 (414),15 | |
Ta-2.5W (RO5252), 40000 (276), 30000 (207), 20 | |
Ta-40Nb (RO5240), 35000 (241), 20000 (138), 25 | |
Customized zvigadzirwa | Zvinoenderana nekudhirowa, Special zvinodiwa kuti zvibvumiranwe nemutengesi uye mutengi. |
Tsanangudzo
Diameter | Diameter Tolerance | Urefu | Kushivirira | |||
forging tsvimbo | Extruded Rods | rolling rod | tsvimbo yevhu | |||
3.0-4.5 | ±0.05 | - | ±0.05 | - | 500-1500 | + 5 |
>4.5-6.5 | ±0.10 | - | ±0.10 | - | 500-1500 | + 5 |
>6.5-10.0 | ±0.15 | - | ±0.15 | - | 400-1500 | + 5 |
>10-16 | ±0.20 | - | ±0.20 | - | 300-1200 | + 5 |
>16-18 | ±1.0 | - | - | ±0.30 | 200-2000 | + 20 |
>18-25 | ±1.5 | ±1.0 | - | ±0.40 | 200-2000 | + 20 |
>25-40 | ±2.0 | ±1.5 | - | ±0.50 | 150-4000 | + 20 |
>40-50 | ±2.5 | ±2.0 | - | ±0.60 | 100-3000 | + 20 |
>50-65 | ±3.0 | ±2.0 | - | ±0.80 | 100-1500 | + 20 |
TafuraⅠChemical Kuumbwa kweTantalum Rod
Chemistry ppm | ||||||||||||
Tsanangudzo | Chief chikamu | Kusachena kunonyanyisa | ||||||||||
Ta | Nb | Fe | Si | Ni | W | Mo | Ti | O | C | H | N | |
Ta1 | Remainder | 300 | 40 | 30 | 20 | 40 | 40 | 20 | 150 | 40 | 15 | 20 |
Ta2 | Remainder | 800 | 100 | 100 | 50 | 200 | 200 | 50 | 200 | 100 | 15 | 100 |
TaNb3 | Remainder | <35000 | 100 | 100 | 50 | 200 | 200 | 50 | 200 | 100 | 15 | 100 |
TaNb20 | Remainder | 170000-230000 | 100 | 100 | 50 | 200 | 200 | 50 | 200 | 100 | 15 | 100 |
Ta2.5W | Remainder | 400 | 50 | 30 | 20 | 30000 | 60 | 20 | 150 | 50 | 15 | 60 |
Ta10W | Remainder | 400 | 50 | 30 | 20 | 110000 | 60 | 20 | 150 | 50 | 15 | 60 |
Tafura Ⅱ Inotenderwa Kusiyana muDiameter yeTantalum Rods
Diameter, inch (mm) | Kushivirira, +/-inch (mm) |
0.125~0.187 kunze (3.175~4.750) | 0.003 (0.076) |
0.187~0.375 kunze (4.750~9.525) | 0.004 (0.102) |
0.375~0.500 kusanganisa (9.525~12.70) | 0.005 (0.127) |
0.500~0.625 kunze (12.70~15.88) | 0.007 (0.178) |
0.625~0.750 kunze (15.88~19.05) | 0.008 (0.203) |
0.750~1.000 kusanganisa (19.05~25.40) | 0.010 (0.254) |
1.000~1.500 kusanganisa (25.40~38.10) | 0.015 (0.381) |
1.500~2.000 kusanganisa (38.10~50.80) | 0.020 (0.508) |
2.000~2.500 kusanganisa (50.80~63.50) | 0.030 (0.762) |
Application
Capacitors;kuvhiya kudyara uye zviridzwa;ink jet nozzles.
Inoshandiswa mumidziyo yerabhoritari.
Inoshandiswa sechinotsiva platinum.
Inoshandiswa mukugadzira super alloys uye electron-beam kunyunguduka.